Tempered glass

Hot dipping treatment is also called homogeneous, commonly known as "ignite". Hot dipping process is toughened glass heated to 290 ℃ plus or minus 10 ℃, and heat preservation time, prompting nickel sulfide quickly complete crystal phase transition in toughened glass, let originally used to detonate the toughened glass after artificially breakage in the factory in advance of the hot-dip furnace, thus reducing after installation of toughened glass in use since the explosion.

General hot air was used as heating medium, the method called "HeatSoakTest" abroad, referred to as "HST, literal translation for the hot dip process.

Processing specifications:

Processing: 8 mm ~ 22 mm thickness

Maximum size: 13000 mm * 2440 mm